聚碳酸酯PC,导电, 阻燃

 

THE-CON 14-030-FR-L

聚碳酸酯

THEMIX Plastics, Inc.

Technical Data

 

产品说明

 

THE-CON 14-030-FR-L is a flame retardant, conductive thermoplastic compound based on a flame retardant polycarbonate (PC) with carbon fibers with a mold release agent. THE-CON 14-030-FR-L can be injection molded without modifications using normal processing conditions as would be used with polycarbonate and glass or carbon fibers. This compound exhibits electrical conductivity suitable for ATEX applications, excellent physical properties with an added mold lubricant. This product is just a sampling of our capabilities. THEMIX can also develop specialty compounds for all your needs.

 

总体

 

材料状态 • 已商用：当前有效

资料 1 •  Technical Datasheet (English)

供货地区 • 北美洲

添加剂 • 脱模 • 阻燃

性能特点 • 导电 • 经润滑 • 阻燃性能

• 导电性 • 脱模性能良好

外观 • 黑色 • 可用颜色 • 自然色

形式 • 颗粒

加工方法 • 注射成型

物理性能 额定值单位制 测试方法

比重 1.26g/cm³ ASTM D792

收缩率

流动 0.40% ASTM D955

-- 0.40% ISO 294-4

机械性能 额定值单位制 测试方法

拉伸模量

-- 8270MPa ASTM D638

-- 8300MPa ISO 527-2

抗张强度

屈服 103MPa ASTM D638

屈服 100MPa ISO 527-2

伸长率 (断裂) 2.0 到 4.0% ASTM D638

ISO 527-2

弯曲模量

-- 7580MPa ASTM D790

-- 7600MPa ISO 178

弯曲强度

-- 159MPa ASTM D790

-- 160MPa ISO 178

冲击性能 额定值单位制 测试方法

悬壁梁缺口冲击强度

0.125 mm 53J/m ASTM D256

0.125 mm 50J/m ISO 180

无缺口悬臂梁冲击 (0.125 mm) 530J/m ASTM D256

ISO 180

热性能 额定值单位制 测试方法

热变形温度 3 (0.45 MPa, 未退火) 140°C ASTM D648

ISO 75-2/Bf

电气性能 额定值单位制 测试方法

表面电阻率 < 1.0E+5ohm ASTM D257

体积电阻率 < 1.0E+4ohm·cm ASTM D257

可燃性 额定值单位制 测试方法

UL 阻燃等级 V-0 UL 94

 

THE-CON 14-030-FR-L

聚碳酸酯

THEMIX Plastics, Inc.

注射 额定值单位制

干燥温度 115 到 127°C

干燥时间 2.0 到 4.0hr

建议的最大水分含量 < 0.050%

加工（熔体）温度 282 到 315°C

模具温度 82.0 到 121°C

注射说明

Injection Pressure: Moderate

 

 

 

 