G-Lex 19 PC
聚碳酸酯
Gardiner Compounds Ltd.
Technical Data
产品说明
G-Lex is a polycarbonate compound that has been made from a specified and approved feedstock for the last fifteen years. It is noted for its high impact resistance over a wide range of temperatures. It has excellent heat resistance and all grades pass the 850oC glow wire test at 1.0mm. The high flow grade is particularly suited to thin wall, long flow length application.
G-Lex complies with all recycling directives and can be recycled in the normal way. After its first application the resin can be reground and reused either in a similar manner or cascaded down for reuse in less demanding applications.
Typical applications include electrical goods, lighting, telecommunications, appliances and security devices and other applications where strength and impact are important.
This material is available in Black and natural and most semi translucent, translucent and opaque colours.
总体
材料状态 • 已商用：当前有效
资料 1 • Technical Datasheet (English)
供货地区 • 欧洲
回收含量 • 是
性能特点 • 抗撞击性，高 • 良好的强度 • 耐热性，高
• 可回收材料 • 流动性高
用途 • 电气/电子应用领域 • 电器用具 • 照明装置
• 电气部件 • 通讯器材
外观 • 半透明 • 黑色
• 不透明 • 自然色
加工方法 • 注射成型
物理性能 额定值单位制 测试方法
密度 1.20g/cm³ ISO 1183
熔流率 (300°C/1.2 kg) 20g/10 min ISO 1133
收缩率 3 0.50 到 0.70% ISO 2577
吸水率 (平衡, 23°C, 85%RH) 0.35% ISO 62
机械性能 额定值单位制 测试方法
拉伸模量 2300MPa ISO 527-2/1
拉伸应力 ISO 527-2/50
屈服 63.0MPa
断裂 > 50.0MPa
拉伸应变 (屈服) 6.0% ISO 527-2/50
冲击性能 额定值单位制 测试方法
悬壁梁缺口冲击强度 (23°C) 12kJ/m² ISO 180/1A
无缺口伊佐德冲击强度 (23°C) 无断裂 ISO 180/1U
热性能 额定值单位制 测试方法
热变形温度 (1.8 MPa, 未退火) 124°C ISO 75-2/A
维卡软化温度 140°C ISO 306/B120
可燃性 额定值单位制 测试方法
UL 阻燃等级 (1.60 mm) HB UL 94
灼热丝易燃指数 (1.00 mm) 850°C IEC 60695-2-12
注射 额定值单位制
干燥温度 120°C
干燥时间 < 4.0hr
建议的最大水分含量 < 0.020%
螺筒后部温度 240 到 265°C
螺筒中部温度 265 到 290°C
螺筒前部温度 275 到 300°C
G-Lex 19 PC
聚碳酸酯
Gardiner Compounds Ltd.
注射 额定值单位制
射嘴温度 265 到 275°C
加工（熔体）温度 310°C
模具温度 80.0 到 100°C
注射说明
Max Dwell Time: 8 mins
备注
1 通过这些链接您能够访问供应商资料。我们尽量保证及时更新资料；不过您可以从供应商处了解最新资料。
2 一般属性：这些不能被视为规格。
3 500 bar
|